Austempering相关论文
Austempering ductile iron (ADI) is an attractive material due to its excellent comprehensive mechanical properties. Howe......
Effect of Cu content on microstructures and mechanical properties of ADI treated by two step austemp
The effect of Cu content on the microstructures and mechanical properties (yield strength, ultimate tensile strength, im......
Effects of austempering temperature on microstructure and surface residual stress of carbidic austem
...
Multiphase microstructure formation and its effect on fracture behavior of medium carbon high silico
This work investigated the evolution of multiphase microstructure and impact fracture behavior of medium carbon high sil......
The thermal stability of an ADI has been studied by isothermal aging at 350℃ for 150 hours, measuring the amount of ret......
The equilibrium partition ratio, k, has been measured for Mn, Mo, Si, Ni and Cu in a ductile iron with composition(wt.%)......
Thermomechanical controlled processing (TMCP) was conducted by using a laboratory hot rolling mill. Austempering in the ......
对热轧后等温淬火的热轧Si—Mn TRIP钢进行了研究，通过对该钢的组织性能检测，讨论了其相变诱发塑性（TRIP）机制．结果表明：热轧Si—Mn TRIP......
铜螺钉冷镦模具在服役过程中承受着多种压缩应力、疲劳应力以及冲击胀力、摩擦力，致使模具容易产生疲劳崩裂及型腔表面磨损、拉毛及......
热 rolledSi-Mn 旅行钢的机械性质上的 austempering 的效果被学习。转变的机制导致了粘性(旅行) 通过微观结构的考试和标本的机械......
通过与常规淬火与回火热处理工艺比较，研究了不同等温淬火热处理工艺对高铬耐磨铸铁的组织与性能的影响，等温淬火热处理工艺可以获得......
等温淬火含硼高硅合金是一种新型的金属耐磨材料,它以高硬度的硼化物耐磨相代替传统的碳化物耐磨相,是在高硅铸钢合金成分的基础上......
用作等温淬火的硝盐浴中含有的水份，影响着球墨铸铁凸轮轴在等温淬火过程中产生的马氏体量，在未经回火的状态下，经受磨削加工极易出现......
本文对经真空淬火、回火和盐浴炉加热等温淬火、回火并达到四种不同硬度要求的30CrMnSiA钢的力学性能进行了系统的试验研究.结果表......
新安装调试的UMS型贝氏体等温淬火网带炉生产线主要由磁性上料机、网带炉、网带盐浴槽、盐回收装置和烘干机组成，其特点是，结构新颖，......
经等温淬火的发动机齿形链,材料为51CrV4钢,在装配过程中发现有断裂现象。对断裂的齿形链进行了化学成分分析、显微组织检验和硬度......
对低碳球铁的等温淬火工艺进行了研究.测定了低碳球铁件在几种不同奥氏体化时间、等温时间下的力学性能,并对金相组织进行了分析.......
The microstructural evolution and consequent changes in strength and ductility of advanced NANOBAIN steel during prolong......
研究了在SME法训练条件下,等温淬火热处理对Cu-Zn-Al形状记忆合金单程形状记忆效应ηO的影响及与'淬火+上淬'热处理的比较......
分析了大齿轮轴渗碳淬火后齿面产生较大畸变的原因,找出了适合预留收缩余量和等温淬火工艺,解决了大齿轮轴的热处理畸变.......
阐述了等温淬火白口铸铁中主要元素的作用及选择原则.研究了锰、铬元素对力学性能的影响以及等温淬火温度对力学性能和抗磨性能的......
低碳球墨铸铁经过900℃奥氏体化,在370℃等温适当时间,空冷到室温后可以获得约84%簇条状铁素体和约16%的残留奥氏体组织.该低碳球......
研究了0．15C-1．5Mn-1．5Al-0．3Si TRIP钢820℃2min加热后快冷至450℃盐浴中保温5～300S空冷的组织和力学性能。结果表明，随在贝氏体转变区4......
根据柱塞套技术要求,制定了柱塞套贝氏体等温淬火工艺,研究了其组织性能特点,并提出了柱塞套贝氏体等温淬火过程控制要点。......
研究了等温淬火温度与时间对球墨可锻铸铁组织和性能的影响.试样成分(WB/%)为:3.0C,1.8 Si,0.4Mn,0.1P,0.1S.采用中频炉熔炼,用稀......
采用正交试验的方法研究了等温淬火工艺参数的变化对低铬变质白口铸铁力学性能的影响。结果表明,淬火加热温度较低或保温时间较短......
含钒TRIP钢热变形后在350～450℃等温处理30min,研究卷取温度对其显微组织和力学性能的影响。结果表明,随等温温度的升高,贝氏体、残......
研究了质量分数为0．4％C、1．5％Si、1．5％Mn、0．95％Cr、添加微量稀土的试验钢的力学性能，试验钢由真空感应炉熔炼，经扩散退火、等温淬火处理后，利......
利用等温回火实验,采集了淬火钢在不同条件下回火时的硬度数据。采用非线性回归分析方法,得到淬火钢的回火硬度与回火温度和回火时......
利用XRD、SEM、TEM、维氏硬度计和拉伸试验机对Fe-1．5C-1．5Cr-2．0Al超高碳钢经300℃等温淬火后的组织及力学性能进行了研究．组织观察与......